THE HEAVY WATER-SLURRY PILE
摘要
in these two regions. Corrosion-test specimens of Zircaloy-2, titanium, and type 347 stainless steel were placed in the loop at three different locations for exposure to three different levels of irradiation. Duplicate sets of specimens in each position were exposed to flow velocities of 8 and 22 fps, respectively. For the in-pile irradiation, thorium oxide containing 0.43 wt of enriched U, based on Th, was used. This thoria-urania was produced by air calcination at l225 deg C of coprecipit.ited oxalates and had a me.in particle size of l.7 mu . A Pd catalyst w-as dispersed in the slurry for liquid-phase recombination of the radiolytic gas. The loop was operated in beam-holc HB-2 of the LlTR from July 19 to October l9, l960. During this period slurry was continuously eireulated at 280 deg C for 2220 hr without incident; 1839 hr were at full reactor power (3 Mwt), at which the estimated average thermal flux over the 300volume core section was 5 x l0/sup 12/ neutrons/cm/sup 2/- see. At the start of in-pile operation the loop was charged to a concei tration of 979 g of Th and 3.83 g of fully enriched U per li (at 280 deg C) which was reduced by sampling to 748 g of Th idnd 2.74 g of U per liter at the end of the irradiiition period bascd on the assunmption that no losses had occurrcd. Siinmples of slurry were withdrawn at intervals for analyses to determine the effects of radiation on the thoria-urania slurry. (auth)