Microstructure and Properties of Hot Working Die Steel H13MOD
摘要
Compared with H13 steel,the influences of different heat treatment process on the microstructure and properties of the new type of hot working die steel H13MOD were studied.The results show that the complete austenitizing temperature of H13MOD is around 1 030℃ and the quenching hardness achieves the maximum value at this temperature.While for H13,the complete austenitizing temperature is above 1 100℃ and the quenching hardness rise constantly with the quenching temperature increasing.In quenching process,the undissolved MC carbides can prevent the coarsening of grain in both steels.With the rise of quenching temperature,when MC carbides dissolve completely,the grain grows quickly.The hardness and strength of H13MOD at higher tempering temperature(above570℃)are nearly the same as those of H13,but its toughness is higher than that of H13.Mo2C carbide is the main strengthening phase in H13MOD,which is attributed to the higher content of Mo.The quantity of VC eutectic carbides is reduced because of lower content of V in H13MOD,which plays an important role in enhancing the impact toughness of H13MOD.Under a certain strength condition,H13MOD steel can be used in the environment that higher toughness is required and the service life of die casting mold can be improved.