Fabrication of A1/A12O3 Composites and FGM
摘要
Al/Al2O3 composites of different ratios were hot-press sintered at 575～640℃ under a pressure of 30 MPa for 2 h in a vacuum furnace. It was found that the relative density of the Al/Al2O3composites could be increased evidently with the rise of sinter temperature. No reaction occurred between Al and Al2O3 at the sinter temperatures. Under 640℃-30 MPa-2 h experimental condition, Al/Al2O3 system FGM was successfully fabricated, and its density range changed quasi-continuously from 2.887x103 kg/m3 to 3.1909x103 kg/m3 within the middle 1.0 mmthickness range.