BARRIER PROPERTIES OF VINYLIDENE CHLORIDE COPOLYMERS
摘要
The permeability coefficients of a series of copolymers of vinylidene chloride (VDC)with methyl acrylate (MA), butyl acrylate (BA) or vinyl chloride (VC) (as comonomer)to oxygen and carbon dioxide have been measured at 1.0 MPa and 30℃, while those towater vapor have been measured at 30℃ and 100% relative humidity All the copolymersare semicrystalline. VDC/MA copolymers have lower melting temperature compared withVDC/BA copolymers, while that melting temperature of VDC/VC copolymer is higherthan that of VDC/acrylate copolymers with the same VDC content. The barrier propertyof the copolymers is predominantly controlled by crystallite, free volume fraction, andcohesive energy The permeability coefficients of VDC/MA copolymers to oxygen, carbondioxide, and water vapor were successfully correlated with the ratio of free volume tocohesive energy.