Research on Calcium Doped Ceria Used in Intermediate-Temperature SOFCs Anodes
摘要
As a mixed ion-electronic conductor, doped ceria, especially rare earth doped ceria, were used as anodes or components of anodes in SOFCs. In this work, calcium doped ceria (CCO) was synthesized to be used in intermediate-temperature SOFCs (IT-SOFCs) anodes in order to reduce the cost of anode-supported SOFCs. Electrical conductivity of 20% calcium doped ceria (20CCO) reached 0.209 S·cm-1 in hydrogen at 850 ℃, and 0.041 S·cm-1 in air at 800 ℃, which is about 0.04 S·cm-1 lower than that of conventional samaria-doped ceria (0.079 S·cm-1). Electrochemical performance of Ni-20CCO cermet as anode was investigated using a fuel cell with 35 μm-thick SDC electrolyte and Sm0.5Sr0.5Co-SDC cathode. Maximum power density was 623 mW·cm-2 under humidified (3% H2O) hydrogen at 650 ℃, inferring high catalytic activity of the Ni-20CCO anode.