Rheology of YBa{sub 2}Cu{sub 3}O{sub 7-x} precursors
摘要
Nitrate and acetate precursors to YBa[sub 2]Cu[sub 3]O[sub 7-x] (123) are prepared using a molten salt technique. The viscosity and shear stress of the paste are controlled by evaporation of water from the paste. The pastes contain [approximately] 20--80 vol % solids. Rheometry over strain rates of 0--200 sec[sup [minus]1] shows both systems are shear-thinning. Both systems are thixotropic. The nitrate system may be described by a two-stage Bingham Plastic model, the acetate by a Hershel-Bulkley model. The existence of more than one region of flow behavior suggests that there are at least two mechanisms which contribute to flow. In the low strain rate region, flow resistance is due to the existence of flocs in the colloidal assembly. At higher strain rates, flow is probably controlled by interlaminar drag interactions. Precursors produced by both methods have been used to form fibers of YBa[sub 2]Cu[sub 3]o[sub 7-x], by ram extrusion.