Influence of oxidant KMnO4 on film—forming process of rare earth metal conversion coating on LY12 aluminum alloy
摘要
A Cu/Al galvanic couple was established to study the influence of the oxidant KMnO4 on the film-forming process of rare earth metal (REM) conversion coating on LY12 aluminum alloy. It is found that the galvanic couple simulative experiment accords with the actual immersion, and it can be substantially used to simulate the behavior of LY12aluminum alloy in the film-forming process. It is showed that the formation of the coating is quickened in CeCl3 solution containing KMnO4 compared with that not containing KMnO4. XPS results reveal that the coating formed on cathode is composed of oxide or hydroxide of Ce and Mn, so the mechanism of formation of REM conversion coating changes when KMnO4 is added.
引用本文（GB/T 7714）
TianzhuGao, JiuqingLi. Influence of oxidant KMnO4 on film—forming process of rare earth metal conversion coating on LY12 aluminum alloy[J]. Acta Scientiarum Naturalium Universitatis Sunyatseni, 2002.
引文网络
本站仅收录题录与摘要供学习参考，全文版权归属出版方；如有侵权请联系我们删除。