Die wall lubricated warm compaction of iron-based powder metallurgy material
摘要
Lubricant is harmful to the mechanical properties of the sintered materials. Die wall lubrication was applied on warm compaction powder metallurgy in the hope of reducing the concentration level of the admixed lubricant. Iron-based samples were prepared by die wall lubricated warm compaction at 175℃, using a compacting pressure of 550MPa. Emulsified polytetrafluoroethylene(PTFE) was used as die wall lubricant. Admixed lubricant concentration ranging from 0 to 0.5% was tested. Extremely low admixed lubricant contents were used. Results show that in addition to the decrease in ejection forces, the green density of the compacts increases with the decrease of admixed lubricant content until it reaches the maximum at 0.06% of lubricant content, then decreases with the decrease of admixed lubricant content. The mechanical properties of the sintered compacts that contain more than 0.06% admixed lubricant are better than those of the samples that contain lesser lubricant. No scoring was observed in all die wall lubricated experiments.